Vias having varying diameters and fills for use with a semiconductor device and methods of forming semiconductor device structures including same

ABSTRACT

A method for forming electrical interconnects having different diameters and filler materials through a semiconductor wafer comprises forming first and second openings through a semiconductor, wherein the first opening has a narrower width (smaller diameter) than the second opening. A first conductive material is formed over the semiconductor wafer to completely fill the narrower opening and only partially fill the wider opening. The first conductive material is optionally removed from the wider opening using an isotropic etch. A second conductive material is subsequently formed over the semiconductor to completely fill the wider opening.

CROSS REFERENCE TO RELATED APPLICATION

This application is a divisional to U.S. patent application Ser. No.11/044,443 filed Jan. 26, 2005, now U.S. Pat. No. 7,348,671.

FIELD OF THE INVENTION

This invention relates to the field of semiconductor manufacture and,more particularly, to a method for forming vias through a semiconductorwafer and the structures resulting from the method.

BACKGROUND OF THE INVENTION

Structures which are increasingly common during the formation of asemiconductor device are conductor-filled vias formed through asemiconductor wafer. The vias provide passageways through thesemiconductor wafer, for example from the front (circuit or active) sideof the wafer to the back side of the wafer. The conductors may passpower or ground connections, or digital or analog signals from the frontof the wafer to the back. These vias may be used with multichip modulesto pass connections or signals between stacked semiconductor dice, or toconnect a node such as a ground node formed on the front of a single dieto the back of the die, which is then connected to a lead frame or otherchip carrier.

Power and ground connections typically require a conductor having alarger diameter than is required for transmission of digital or analogsignals due to higher current loads needed for power and groundconnections than for signals. To conserve space on the surface of asemiconductor die, it is desirable to form digital and analog signalvias at a smaller size than power and ground connection vias. However,this approach requires additional processing, as the first type of viamust be formed and filled before forming and filling the second type ofvia. Additional manufacturing complexity is required to fill the viaswith different types of materials, for example copper within signal viasand a tin-lead alloy within power and ground connection vias.

A method which enables the simultaneous formation of different sizedvias with different metallization, and structures resulting from themethod, would be desirable.

SUMMARY OF THE INVENTION

The present invention comprises a method which, among other advantages,simplifies the formation of conductively filled openings or vias havingmore than one diameter. In accordance with one embodiment of theinvention at least first and second vias are mechanically or chemicallyetched through a semiconductor wafer, with the first via having anarrower width than the second via. A conformal liner which electricallyisolates the material of the wafer from the two vias is formed, then afirst metallization is provided to completely fill the narrower firstvia and to only partially fill the second, wider via. A secondmetallization is provided to completely fill the remainder of thesecond, wider via but does not enter the first via, which was previouslycompletely filled with the first metallization. Subsequent processing ofthe wafer may then continue, as known to those of ordinary skill in theart.

The present invention further comprises a structure in which a firstopening is filled with a first conductor and a second opening, which iswider than the first opening, is filled with a second conductor which isdifferent from the first conductor. Various embodiments arecontemplated, including embodiments having both the first and secondconductor in the second opening, only the second conductor in the secondopening, and various layers used for the first and second conductorincluding first and second conductors which each comprise more than oneconductive layer.

Additional advantages will become apparent to those skilled in the artfrom the following detailed description read in conjunction with theappended claims and the drawings attached hereto.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1-4 are cross sections depicting various intermediate in-processstructures resulting from a first embodiment of the invention;

FIG. 5-8 are cross sections depicting various intermediate in-processstructures resulting from a second embodiment of the invention;

FIGS. 9-13 are cross sections depicting an intermediate in-processstructure which results from a third embodiment of the invention;

FIGS. 14-25 are cross sections depicting an intermediate in-processstructure which results from another embodiment of the invention

FIG. 26 is an isometric depiction of various components which may bemanufactured using devices formed with an embodiment of the presentinvention; and

FIG. 27 is a block diagram of an exemplary use of the invention to formpart of a memory device having a storage transistor array.

It should be emphasized that the drawings herein may not be to exactscale and are schematic representations. The drawings are not intendedto portray the specific parameters, materials, particular uses, or thestructural details of the invention, which can be determined by one ofskill in the art by examination of the information herein.

DETAILED DESCRIPTION OF THE ILLUSTRATED EMBODIMENTS

The term “wafer” is to be understood as a semiconductor-based materialincluding silicon, silicon-on-insulator (SOI) or silicon-on-sapphire(SOS) technology, doped and undoped semiconductors, epitaxial layers ofsilicon supported by a base semiconductor foundation, and othersemiconductor structures. Furthermore, when reference is made to a“wafer” in the following description, previous process steps may havebeen utilized to form regions or junctions in or over the basesemiconductor structure or foundation. Additionally, when reference ismade to a “substrate assembly” in the following description, thesubstrate assembly may include a wafer with layers including dielectricsand conductors, and features such as transistors, formed thereover,depending on the particular stage of processing. In addition, thesemiconductor need not be silicon-based, but could be based onsilicon-germanium, silicon-on-insulator, silicon-on-sapphire, germanium,or gallium arsenide, among others. Further, in the discussion and claimsherein, the term “on” used with respect to two layers, one “on” theother, means at least some contact between the layers, while “over”means the layers are in close proximity, but possibly with one or moreadditional intervening layers such that contact is possible but notrequired. Neither “on” nor “over” implies any directionality as usedherein. Further, the terms “via” and “opening” are used hereininterchangeably.

A first embodiment of an inventive method for forming vias having twodifferent diameters and fills is depicted in FIGS. 1-4. FIG. 1 depicts asemiconductor wafer 10 and a patterned photoresist layer 12 on a majorsurface of the semiconductor wafer 10. In this embodiment thephotoresist layer comprises first openings 14 having a first diameterand second openings 16 having a second diameter which is larger than thefirst diameter. The openings will typically have a round, oval, or ovateshape; however, other configurations and physical arrangements of thewide and narrow openings are possible depending on their eventual useand the design of the semiconductor device. The first openings 14 mayhave a diameter (width) of between about 10 micrometers (μm) and about50 μm, while the second openings 16 may have a diameter (width) ofbetween about 50 μm and about 100 μm, such dimensional ranges beingexemplary only and not limiting of the present invention.

After forming the FIG. 1 structure, openings are formed in the wafer 10using any suitable method. For example, the openings may be etched intothe wafer using a dry chemical etch comprising the use of sulfurhexafluoride (SF₆) and/or tetracarbon hexafluoride (C₄F₆), a drymechanical etch with an inert material such as argon, or with wet etchesusing potassium hydroxide (KOH) or tetra-methyl ammonium hydroxide(TMAH). The openings may also be formed using laser ablation with asolid state laser (seven watt diode-pumped laser at 355 nanometerwavelength), or with other micromachining methods such as electricaldischarge machining (EDM). After etching the openings, the photoresistlayer is removed to result in the FIG. 2 structure comprising firstopenings 20 having a first diameter and second openings 22 having asecond diameter which is larger than the first diameter. With thisexemplary embodiment, the first openings 20 will define signalconnections while the second openings 22 will define power and groundconnections. While this embodiment depicts the openings etchedcompletely through the wafer, a partial etch through the wafer followedby a wafer back grind to expose the openings from the back side of thewafer is contemplated as being suitable, and is described below withreference to a later embodiment.

After forming the FIG. 2 structure, a conformal dielectric isolationlayer 30 is formed to electrically isolate the semiconductor wafer 10from subsequently-formed conductive layers. Dielectric layer 30 maycomprise a layer formed using tetraethyl orthosilicate (TEOS), a lowsilane oxide (LSO) formed using chemical vapor deposition (CVD), or apulsed deposition layer (PDL) oxide. Other contemplated materials fordielectric isolation layer 30 include nitrides formed using atomic layerdeposition (ALD), and parylenes such as PDL Parylene HT™. Regardless ofthe material used for dielectric layer 30, the formation of dielectriclayer is preferably performed at a temperature of less than 250° C., andmore preferably below about 175° C. to prevent damage to structureswhich have been previously formed on the wafer. With the openings havingthe exemplary target diameters described above, isolation layer 30 mayhave a target thickness of between about 0.25 μm and about 2.0 μm or,more preferably, between about 0.5 μm and about 1.0 μm.

Next, any required adhesion layer (not individually depicted) is formed,then a barrier layer 32 is formed as depicted in FIG. 3. A barrier suchas physical vapor deposition (PVD) tungsten or tantalum may be desiredto prevent electromigration of metal from a subsequently-formed copperconductor layer to dielectric 30, then to wafer 10. An adhesion layermay be formed if needed to ensure a the barrier does not separate fromthe dielectric, or to ensure a later-formed metal does not separate fromthe barrier layer. Each of the barrier layer and the adhesion layer (ifformed) may be between about 125 angstroms (Å) and about 225 Å, and morepreferably between about 150 Å and about 200 Å thick. Either layer maybe formed using chemical vapor deposition (CVD) or atomic layerdeposition (ALD).

After forming a barrier layer 32 or an adhesion layer if desired, aconductive seed layer 34 comprising one or more layers of material isformed on the isolation layer. With the diameter of the openingdescribed above, the first conductive seed layer has a target thicknessof between about 1,000 Å and about 2,500 Å thick, and more preferablybetween about 1,500 Å and about 2,000 Å. One preferred seed layercomprises 2,000 Å PVD copper followed by 400 Å electroless copperplating. The plating functions as a seed layer enhancement (SLE) to fillany discontinuities in the PVD film, particularly in the deepest partsof the vias. Next, one or more metal layers 36 are formed to asufficient thickness to fill the narrow openings, but to leave the wideropenings unfilled. Thus metal layer 36 will be of a thickness equivalentto at least half the width of the first openings 20 which remain afterforming layers 30-34. As the total thickness of the isolation layer, thebarrier layer, and the seed layer for this exemplary embodiment isbetween about 0.5 μm and about 2.5 μm compared to the width of each ofthe first openings 20 which is between about 10 μm and about 50 μm, thefill layer will be formed to have a minimum thickness of between about4.5 μm and about 24.5 μm, depending on the width of the first openings20 in the wafer. One exemplary metal layer 36 may comprise 1 μm ofcopper and 5 μm of nickel, each deposited using electrochemicaldeposition (ECD) according to techniques known in the art. Thecombination of nickel on copper aids in stress reduction in the vias,for example stress placed on the wafer during conductor formation andsheer stress placed on the layers lining the openings in the wafer whichmay cause them to delaminate.

After forming the first conductive layer seed layer 34 and metal layer36 to fill the first openings 20 and performing any subsequent desiredor required processing, a second conformal conductive layer 38 is formedas depicted in FIG. 3. As the second openings 22 will define relativelyhigh current capacity interconnects, a conductor such as a tin/leadsolder or another layer providing low resistance and high reliabilitymay be preferred. Second conductor layer 38 is preferably formed using awave solder process, or may be formed using other suitable solderprocessing methods. Other metals which may function sufficiently in thisexemplary embodiment include silver, gold, cobalt, nickel, copper, etc.Second conductive layer 38 is formed to a sufficient thickness to resultin the complete filling of the second openings 22. With this exemplaryembodiment, the second conductive layer is formed to a thickness ofbetween about 20 μm and about 40 μm. FIG. 3 depicts a structure withboth first conductive layer 36 and second conductive layer 38 within thesecond openings 22; however, other layers may be present within eitherof the openings (for example adhesion layers or enhancement layers toimprove electrical conduction).

After forming the FIG. 3 structure the layers overlying the horizontalsurface of the wafer may be removed, for example using an abrasivetechnique such as mechanical planarization or chemical-mechanicalplanarization (CMP) in accordance with means known in the art, to resultin the structure of FIG. 4. Any subsequent desired or required waferprocessing is then continued according to means known in the art toresult in a functional semiconductor device, and includes the connectionof signals, power, or ground to the conductors, for example low currentconnections to the narrower conductors 42 and higher current connectionsto the wider conductors 44.

Another embodiment is depicted by FIGS. 5-8. The structure of FIG. 5 isformed according to the description above, stopping just prior to thestep of forming metal layer 38 of FIG. 3. The FIG. 5 structure isplanarized, for example using an abrasive technique such as CMP. Thismay require the formation of a protective layer such as oxide orphotoresist within wider, unfilled openings 22 prior to planarization,and the protective layer may be removed after planarization. Thestructure of FIG. 5 is planarized and any protective material withinopenings 22 is removed to result in the FIG. 6 structure. A second metallayer 70 is formed as depicted in FIG. 7, for example in a similarmanner as that described for layer 38 above. Layer 70 may also be formedusing a damascene process (i.e. a blanket deposition and subsequent CMPor other planarization) to result in the narrow 72 and wide 74conductive lines or plugs having a selected pattern which depends on theintended use of the device and conductors.

Another embodiment is depicted by FIGS. 9-13 and results in the removalof layer 36 of FIG. 3 from the second openings 22, while leaving layer36 within the first openings 20. In this embodiment, first 20 and second22 openings are etched into a semiconductor wafer 10 to result in thesemiconductor wafer substrate assembly of FIG. 9. Dielectric isolation30, barrier layer 32, seed layer 34, and first conductive layer 36 arethen formed in accordance with the embodiment of FIGS. 1-4 to result inthe structure of FIG. 10. At this point the first conductive layer 36 isformed to bridge the first openings 20, and is formed within, but doesnot bridge, the second openings 22.

The FIG. 10 structure is then exposed from the active surface to anisotropic etch of layer 36 to result in the FIG. 11 structure. A wetetch such as exposure to an acid comprising a dilute mixture of nitricacid (HNO₃), hydrofluoric acid (HF), and acetic acid (CH₃COOH, HAc)would be sufficient. Because layer 36 fills the first openings 20 anddeposits on the horizontal surface of the wafer over the first openings20, an etchant will remove layer 36 from within the second openings 22and from the horizontal surface of the wafer substrate assembly 10, butwill leave the conductor within the first openings 20 (unless an overetch is performed, which is to be avoided in this embodiment).

After forming the FIG. 11 structure, a second conductive layer 120 isformed, for example using techniques described above for layer 38, toresult in the structure of FIG. 12. Finally, a vertical anisotropicetch, a CMP, or a planarization and an isotropic etch is performed toresult in the structure of FIG. 13. This embodiment is useful if thematerial of layer 36 would result in a conductor within the secondopenings 22 which is less desirable than having the second openings 22substantially completely filled with the material of layer 120. Forexample, if the material of layer 36 has a lower melting temperature,higher resistance, or breaks down more readily under current which willbe applied to the conductor in the wider openings than the material oflayer 120, this embodiment enables removal of the material of layer 36to result in a more complete fill of second openings 22 with thematerial of layer 120.

Another embodiment of the invention is depicted in FIGS. 14-25. FIG. 14depicts a semiconductor wafer substrate assembly comprising asemiconductor wafer 140, a dielectric passivation layer 142, first 144and second 146 bond pads each having an opening etched therethrough, andan overlying dielectric layer 148 which has been patterned to expose thebond pads 144, 146. As depicted, the opening in the first bond pad 144is narrower (i.e. a smaller diameter for round openings) than theopening in the second bond pad 146. In this embodiment the bond pads areabout 100 μm square, the opening in the first bond pad has a diameter ofbetween about 10 μm and 50 μm, and the opening in the second bond padhas a diameter between of about 50 μm and 75 μm, with the opening in thefirst bond pad 144 having a smaller diameter than the opening in thesecond bond pad 146. This structure can be manufactured by one ofordinary skill in the art from the description herein.

A patterned photoresist mask 150 is formed over the FIG. 14 structure asdepicted in FIG. 15. Mask 150 aligns with the edges of the openings inthe first 144 and second 146 bond pads. Subsequently, an etch isperformed to remove the exposed dielectric passivation 142 andsemiconductor wafer 140 as depicted in FIG. 16 to form a first opening160 and a second opening 162 in the wafer 140, with the second opening162 being wider than the first opening 160. The mask 150 is then removedto result in the structure of FIG. 16.

A dielectric layer 170 such as a PDL oxide layer between about 2,000 Åand about 12,000 Å, preferably about 10,000 Å, is formed over exposedsurfaces, then a patterned photoresist mask 172 is formed to reflect thepattern of dielectric layer 148 as depicted in FIG. 17. Mask 172protects portions of dielectric layer 170 which would be otherwiseexposed and functions to passivate the top side surface of the die. Avertical anisotropic spacer etch is performed on the dielectric layer170 to form dielectric spacers 180 as depicted in FIG. 18 along thevertically-oriented sidewalls of the openings which will electricallyisolate subsequently-formed conductor from the wafer. Next, thephotoresist layer 172 is removed to result in the FIG. 18 structure. Thespacer etch may comprise the use of carbon tetrafluoride (CF₄), chlorine(Cl₂), boron trichloride (BCl₃), and argon in a chamber having anatmospheric pressure of about 15 millitorr with about 10 torr ofbackside pressure. During the etch the temperature of the chamber wallsis maintained at about 80° C. with about a 30° C. cathode. Bias power ismaintained at about 250 watts, with about 1,200 watts of source power.For a PDL oxide used for dielectric layer 170 as described above, theetch is performed for about 260 seconds. This etch may be optimized byone of ordinary skill in the art.

Next, a seed layer 190 is deposited over the surface of the FIG. 18structure as depicted in FIG. 19. The seed layer may comprise 150 Å oftantalum, 2,000 Å of PVD copper, and 400 Å of ECD copper, with the ECDcopper functioning as a seed layer enhancement. Mask layer 192 is thenformed to cover oxide layer 148 and the portions of dielectric layer 170and seed layer 190 which cover oxide 148 as depicted in FIG. 19.

After forming the FIG. 19 structure, a metallization process isperformed which results in a conductive layer forming on exposedportions of seed layer 190. This results in the metal layer 200 of FIG.20. One preferred metal layer 200 comprises the formation of 1 μm ofcopper using an ECD process, and 5 μm of nickel using an ECD process.During this process the metal bridges the first opening 160, but formsconformally within the second opening 162 as depicted in FIG. 20. Tobridge the opening, the metal layer must be formed to have a targetthickness of at least half the width of the first opening 160 whichremains after forming layers 170 and 190. Subsequently, the photoresistmask 192 is removed to result in the FIG. 21 structure.

A wet strip of the exposed seed layer is performed, for example using amixture of hydrofluoric acid, hydrogen peroxide, and propylene glycol toresult in the FIG. 22 structure. A vent 230 is then formed from the backside of the wafer to the bottom of the second opening 162 as depicted inFIG. 23. The vent is preferably formed using a laser, but the back ofthe wafer may also be masked and etched using either a dry or a wetetch. The wafer of FIG. 23 is then processed with the back side of thewafer facing up through a wave solder process to form metal, in thisembodiment a tin/lead solder, within the second opening 162. The vent inthe back of the wafer allows air to escape such that the solder 240 willfill the second opening 162 as depicted in FIG. 24. While the solder isalso depicted in smaller voids formed from removal of mask 190 andexposed portions of layer 192, this layer may not form within thesesmaller voids. If not filled during this process, they will be filledduring a subsequent passivation. Further, the solder 240 will adhere tothe top of metal 200 which fills the first opening 160 to form ameniscus which may facilitate improved electrical connection duringsubsequent processing. Other metal layers may also be used to fill thesecond openings 162 instead of the solder process.

After filling the second opening 162 with metal 240, the wafer is background to erode the wafer surface to expose metal 200 and metal 240 fromthe back side of the wafer as depicted in FIG. 25. This facilitatespassing a signal from one side of the wafer to the other through metal200 and metal 240 within the first 160 and second 162 openings. Thefirst opening 160 in this embodiment is filled with a low resistanceconductor, while the second opening 162 is filled with a more reliableconductor, for example one which can withstand higher current. One useof the present process allows for the passage of a digital signalthrough the metal 200 in the first opening 160, and allows power to bepassed through the metal 240 in the second opening 162. Other uses ofthe present embodiment may also be possible.

As depicted in FIG. 26, a semiconductor device 260 formed in accordancewith the invention may be attached along with other devices such as amicroprocessor 262 to a printed circuit board 264, for example to acomputer motherboard or as a part of a memory module used in a personalcomputer, a minicomputer, or a mainframe 266. FIG. 26 may also representuse of device 260 in other electronic devices comprising a housing 266,for example devices comprising a microprocessor 262, related totelecommunications, the automobile industry, semiconductor test andmanufacturing equipment, consumer electronics, or virtually any piece ofconsumer or industrial electronic equipment.

The process and structure described herein can be used to manufacture anumber of different structures which comprise a structure formed using aphotolithographic process. FIG. 27, for example, is a simplified blockdiagram of a memory device such as a dynamic random access memory havingdigital and analog connections, power/ground connections, and otherfeatures which may be formed using an embodiment of the presentinvention. The general operation of such a device is known to oneskilled in the art. FIG. 27 depicts a processor 262 coupled to a memorydevice 260, and further depicts the following basic sections of a memoryintegrated circuit: control circuitry 270; row 272 and column 274address buffers; row 276 and column 278 decoders; sense amplifiers 280;memory array 282; and data input/output 284.

While this invention has been described with reference to illustrativeembodiments, this description is not meant to be construed in a limitingsense. Various modifications of the illustrative embodiments, as well asadditional embodiments of the invention, will be apparent to personsskilled in the art upon reference to this description. For example, theopenings in the wafer may be etched only partially into the wafer, thencompleted by removal of wafer material from the back of the wafer eitherbefore or after forming the conductors within the openings. It istherefore contemplated that the appended claims will cover any suchmodifications or embodiments as fall within the true scope of theinvention.

1. A method of creating a semiconductor device on a semiconductor wafer,the method comprising: creating at least one first opening and at leastone second opening therein, the at least one first opening having awidth that is narrower than a width of the at least one second opening;forming a dielectric portion within the at least one first opening andwithin the at least one second opening; forming a first conductiveportion over the semiconductor wafer, the first conductive portionpartially filling the at least one second opening and completely fillingthe at least one first opening; forming, prior to forming the firstconductive portion, a barrier portion on the dielectric portion;subsequent to forming the first conductive layer, forming a secondconductive layer over the semiconductor wafer and within the at leastone second opening; removing the first and second conductive portionsfrom over a major surface of the semiconductor wafer through which theat least one first opening and the at least one second opening areexposed while leaving the first conductive portion within the at leastone first opening to form at least one first interconnect and leavingthe at least one second conductive portion within the at least onesecond opening to form at least one second interconnect; electricallyconnecting the at least one first interconnect with one of a digital andan analog signal path; and electrically connecting the at least onesecond interconnect with one of a power and a ground path.
 2. A methodfor use in fabrication of a semiconductor device, the method comprising:etching a major surface of a semiconductor wafer to form at least onefirst opening and at least one second opening at least partiallytherethrough, wherein the at least one first opening has a narrowerwidth than the at least one second opening; forming a substantiallyconformal portion comprising a first conductor, the first conductorforming simultaneously within the at least one first opening and withinthe at least one second opening in the semiconductor wafer andsubstantially fills the at least one first opening and only partiallyfills the at least one second opening; and forming a second conductorwithin the at least one second opening by filling the partially filledat least one second opening with a solder material.
 3. The method ofclaim 2 further comprising, prior to forming the substantially conformalportion comprising the first conductor: forming a conformal dielectricportion over the semiconductor wafer and within the at least one firstopening and the at least one second opening in the semiconductor wafer;etching the conformal dielectric portion to form dielectric spacersalong vertically-oriented sidewalls of the at least one first openingand the at least one second opening to electrically isolate the firstconductor and second conductor within the at least one first opening andthe at least one second opening from the semiconductor wafer.
 4. Amethod for use in fabrication of a semiconductor device, the methodcomprising: etching a major surface of a semiconductor wafer to form atleast one first opening and at least one second opening at leastpartially therethrough, wherein the at least one first opening has anarrower width than the at least one second opening; forming asubstantially conformal portion comprising a first conductor, the firstconductor forming simultaneously within the at least one first openingand within the at least one second opening in the semiconductor waferand substantially fills the at least one first opening and onlypartially fills the at least one second opening; forming a secondconductor which is different from the first conductor within the atleast one second opening; subsequent to forming the first conductor andprior to forming the second conductor, removing a portion of thesemiconductor wafer from a back side of the semiconductor wafer toprovide a vent opening into the at least one second opening whichextends from the back side of the wafer to the at least one secondopening; and placing the semiconductor wafer into a solder wavecomprising the second conductor to fill the second opening with thesecond conductor from a mouth of the at least one second opening.
 5. Amethod for use in fabrication of a semiconductor device, the methodcomprising: etching a major surface of a semiconductor wafer to form atleast one first opening and at least one second opening at leastpartially therethrough, wherein the at least one first opening has anarrower width than the at least one second opening, and wherein the atleast one first opening and the at least one second opening are etchedthrough openings in first and second bond pads located on the majorsurface of the semiconductor wafer; forming a substantially conformalportion comprising a first conductor, the first conductor formingsimultaneously within the at least one first opening and within the atleast one second opening in the semiconductor wafer and substantiallyfills the at least one first opening and only partially fills the atleast one second opening; etching the first conductor to remove thefirst conductor from within the at least one second opening and leavingthe first conductor within the at least one first opening; and forming asecond conductor which is different from the first conductor within theat least one second opening.
 6. A method for use in fabrication of asemiconductor device, the method comprising: etching a major surface ofa semiconductor wafer to format least one first opening and at least onesecond opening at least partially therethrough, wherein the at least onefirst opening has a narrower width than the at least one second opening,and wherein the at least one first opening and the at least one secondopening are completely etched through the semiconductor wafer; forming asubstantially conformal portion comprising a first conductor, the firstconductor forming simultaneously within the at least one first openingand within the at least one second opening in the semiconductor waferand substantially fills the at least one first opening and onlypartially fills the at least one second opening; and forming a secondconductor which is different from the first conductor within the atleast one second opening.
 7. A method for use in fabrication of asemiconductor device, the method comprising: etching a major surface ofa semiconductor wafer to form at least one first opening and at leastone second opening at least partially therethrough, wherein the at leastone first opening has a narrower width than the at least one secondopening; forming a conformal dielectric portion within the at least onefirst opening and the at least one second opening in the semiconductorwafer; etching the conformal dielectric portion to form spacers alongsidewalls of the at least one first opening and the at least one secondopening; forming an electromigration barrier comprising a materialselected from the group consisting of tungsten or tantalum on thespacers; forming a substantially conformal portion comprising a firstconductor, the first conductor forming simultaneously within the atleast one first opening and within the at least one second opening inthe semiconductor wafer and substantially fills the at least one firstopening and only partially fills the at least one second opening,wherein during the formation of the substantially conformal portioncomprising the first conductor the electromigration barrier is incontact with the first conductor; and forming a second conductor whichis different from the first conductor within the at least one secondopening.
 8. A method for use in fabrication of a semiconductor device,the method comprising: etching a major surface of a semiconductor waferto form at least one first opening and at least one second opening atleast partially therethrough, wherein the at least one first opening hasa narrower width than the at least one second opening; forming asubstantially conformal portion comprising a first conductor, the firstconductor forming simultaneously within the at least one first openingand within the at least one second opening in the semiconductor waferand substantially fills the at least one first opening and onlypartially fills the at least one second opening; etching the firstconductor within the at least one second opening in the semiconductorwafer while simultaneously etching the first conductor overlying the atleast one first opening to remove the first conductor from the at leastone second opening in the semiconductor wafer and leaving the firstconductor within the at least one first opening in the semiconductorwafer; and forming a second conductor which is different from the firstconductor within the at least one second opening.
 9. A method for use infabrication of a semiconductor device, the method comprising: etching amajor surface of a semiconductor wafer to form at least one firstopening and at least one second opening at least partially therethrough,wherein the at least one first opening has a narrower width than the atleast one second opening; forming a substantially conformal portioncomprising a first conductor, the first conductor forming simultaneouslywithin the at least one first opening and within the at least one secondopening in the semiconductor wafer and substantially fills the at leastone first opening and only partially fills the at least one secondopening, wherein the formation of the substantially conformal portioncomprising the first conductor comprises: forming a first copper portionusing a physical vapor deposition process; forming a second copperportion on the first copper layer using an electroless copper platingprocess; forming a third copper portion on the second copper portionusing an electrochemical deposition process; and forming a nickelportion on the third copper portion using an electrochemical depositionprocess; and forming a second conductor which is different from thefirst conductor within the at least one second opening.
 10. A method ofcreating a semiconductor device on a semiconductor wafer, the methodcomprising: creating at least one first opening and at least one secondopening therein, the at least one first opening having a width that isnarrower than a width of the at least one second opening; forming adielectric portion within the at least one first opening and within theat least one second opening; forming a first conductive portion over thesemiconductor wafer, the first conductive portion partially filling theat least one second opening and completely filling the at least onefirst opening; forming, prior to forming the first conductive portion, abarrier portion on the dielectric portion; and subsequent to forming thefirst conductive portion filling the at least one second opening withsolder.